Author/Editor | Cotič, Jasna; Jevnikar, Peter; Kocjan, Andraž; Kosmač, Tomaž | |
Title | Complexity of the relationships between the sintering-temperature-dependent grain size, airborne-particle abrasion, ageing and strength of 3Y-TZP ceramics | |
Type | članek | |
Vol. and No. | Letnik 32, št. 4 | |
Publication year | 2016 | |
Volume | str. 510-518 | |
ISSN | 0109-5641 - Dental materials : official publication of the Academy of Dental Materials | |
Language | eng | |
Abstract | Objectives. This study was designed to explore the complex relationships between the sintering-temperature-dependent grain size, airborne-particle abrasion, ageing and strength of 3Y-TZP ceramics. Methods. Biomedical grade 3Y-TZP powder was used to fabricate 180 discs. Half of them were sintered at 1400 % C for 2 h and half at 1500 % C for 2 h. A total of 18 groups of 10 were formed and subjected to the fully crossed experimental protocol of airborne-particle abrasion with Al 2 O 3 at 2.5 bar (no abrasion, 50 % m, 110 % m) and accelerated ageing at 134 % C (no ageing, 12 h, 48 h). The relative amount of monoclinic phase was determined with XRD. The biaxial flexural strength was measured and statistically analyzed using the three-way ANOVA followed by predetermined contrasts and Tukey%s HSD test ( % = 0.05). Results. The low-temperature-sintered, fine-grained ceramic exhibited an excellent age- ing resistance, while the high-temperature-sintered, coarse-grained ceramic experienced a higher surface strengthening and a substantially improved ageing resistance with respect to the airborne-particle abrasion. The overall performance of this material was superior. Significance. Our results show that the sintering temperature has a minor effect on the flex- ural strength, but it plays a crucial role in the surface strengthening and the ageing behaviour of 3Y-TZP dental ceramics. | |
Keywords | 3Y-TZP ceramics sintering grain size 3Y-TZP keramika sintranje velikost zrn |